  • 钻探钻头用钎料
  • 使用说明  
  • 我公司生产的JH系列钻探钻头用钎料,主要用于石油、煤炭、黄金及其他各种地质勘探、钻井、采掘、取芯钻头生产的浸渍钎焊。这类钎料对结构钢和特硬合金粉末,具有良好的浸润性;对金刚石单晶及复合片,具有良好的包嵌及烧结性能,具有良好的强度。 钎焊前,母材表面须清理干净,钎焊温度推荐在液相线以上30~50℃,根据钎焊方法进行调整。
  • Braze welding materials for drilling bit
  • Guideline
  • Braze welding materials for JH series drilling bits are main used in exploit oil, coal, gold and geological prospecting, well drilling, excavating, core bit. These braze welding materials has good invasion property used for constructional steel and hard alloy powder, good wrapping property, sintering property and strength used for monocrystalline diamond and PDC. The matrix must be clean up before welding, the welding temperature can be 30~50 degrees more than liquidus, and make ajustment according to the welding method.
  • 钻探钻头用钎焊料的分类、型号、代号、熔化温度(表1) 
  • 分类 型号 企业代号 通用名 熔化温度(表1)
    铜镍锰 B-Cu60NiMn JH-3 1030-1080℃
    B-Cu61NiMn JH-2 102 1150-1200℃
    铜镍锡锰 B-Cu78NiSnMn JH-5 516 1050-1100℃
    铜镍锌锰 B-Cu50NiZnMn JH-1 1050-1120℃
    B-Cu58NiZnMn JH-7 930-980℃
    B-Cu70NiZnMn JH-6 930-970℃
    B-Cu55NiZnMn JH-4 905-940℃
    铜镍锌锰硅 B-Cu55NiZnMnSi CX-55 910-930℃
    1.2 The classification, grade, code, common name and melting tempreture of braze welding materials used for drilling bits (Tab 1).

    Classification Grade Code Common name Melting tempreture (Tab 1)
    Cu,Ni,Mn B-Cu60NiMn JH-3 1030-1080℃
    B-Cu61NiMn JH-2 102 1150-1200℃
    Cu,Ni,Sn,Mn B-Cu78NiSnMn JH-5 516 1050-1100℃
    Cu,Ni,Zn,Mn B-Cu50NiZnMn JH-1 1050-1120℃
    B-Cu58NiZnMn JH-7 930-980℃
    B-Cu70NiZnMn JH-6 930-970℃
    B-Cu55NiZnMn JH-4 905-940℃
    Cu,Ni,Zn,Mn,Si B-Cu55NiZnMnSi CX-55 910-930℃

  • 化学成分(表2)
  • 分类 型号 企业代号 化学成分(%)
    Cu Ni Mn Zn Si Sn 杂质总量
    铜镍锰 B-Cu60NiMn JH-3 余量 19.0-21.0 19.0-21.0 ≤0.2
    B-Cu61NiMn JH-2 余量 26.0-28.0 10.0-12.0 0.6-1.0 ≤0.2
    铜镍锡锰 B-Cu78NiSnMn JH-5 余量 10.0-12.0 5.0-6.5 0.5-1.5 5.5-6.5 ≤0.2
    铜镍锌锰 B-Cu50NiZnMn JH-1 48.0-51.5 14.0-16.0 23.5-26.5 余量 ≤0.2
    B-Cu58NiZnMn JH-7 57.0-59.0 4.0-6.0 3.5-5.5 余量 ≤0.2
    B-Cu70NiZnMn JH-6 56.0-72.0 6.8-7.8 14.5-15.5 余量 ≤0.2
    B-Cu55NiZnMn JH-4 52.0-55.0 8.0-9.0 5.0-6.0 余量 ≤0.2
    铜镍锌锰硅 B-Cu55NiZnMnSi CX-55 54.0-56.0 6.0-8.0 4.0-6.0 余量 ≤0.2

    化学成分应符合上表的规定,如果用户有特殊要求时,可按供货合同执行。

     1.3 chemical composition (Tab 2)

    Classification Grade Code Chemical composition(%)
    Cu Ni Mn Zn Si Sn impurity
    Cu,Ni,Mn B-Cu60NiMn JH-3 Surplus 19.0-21.0 19.0-21.0 ≤0.2
    B-Cu61NiMn JH-2 Surplus 26.0-28.0 10.0-12.0 0.6-1.0 ≤0.2
    Cu,Ni,Sn,Mn B-Cu78NiSnMn JH-5 Surplus 10.0-12.0 5.0-6.5 0.5-1.5 5.5-6.5 ≤0.2
    Cu,Ni,Zn,Mn B-Cu50NiZnMn JH-1 48.0-51.5 14.0-16.0 23.5-26.5 Surplus ≤0.2
    B-Cu58NiZnMn JH-7 57.0-59.0 4.0-6.0 3.5-5.5 Surplus ≤0.2
    B-Cu70NiZnMn JH-6 56.0-72.0 6.8-7.8 14.5-15.5 Surplus ≤0.2
    B-Cu55NiZnMn JH-4 52.0-55.0 8.0-9.0 5.0-6.0 Surplus ≤0.2
    Cu,Ni,Zn,Mn,Si B-Cu55NiZnMnSi CX-55 54.0-56.0 6.0-8.0 4.0-6.0 Surplus ≤0.2

    Chemical composition should conforms with the regulations above, we alos can acoording to client's request

    1.4 产品供应规格 

    1.4.1 块状钎料规格及允许误差按以下规定执行(表3)

    厚度(mm) 宽度(mm) 长度(mm)
    基本尺寸 允许偏差 基本尺寸 允许偏差 基本尺寸 允许偏差
    2.5、4、5、6、8、10、12、15 ±0.5 10、12、16、20、22、25、30、35、40 ±1 10、12、16、20、22、25、30、35、40 ±1
    1.4 Specification
    T(mm) W(mm) L(mm)
    Size Allowance Size Allowance Size Allowance
    2.5、4、5、6、8、10、12、15 ±0.5 10、12、16、20、22、25、30、35、40 ±1 10、12、16、20、22、25、30、35、40 ±1
      1.4.2 粒状钎料有1~20毫米各种规格。
      1.4.2 Specification of granular braze weling materials is from 1-20mm.
      1.4.3 各种型号钎料可按需方要求协商供应其它规格。
      1.4.3 Special specification according to client's request.